BMC Oral Health Jun 2024Failure of orthodontic bracket bonds is a common occurrence during orthodontic treatment. This study investigated the impact of Er: YAG laser-based removal of adhesive... (Comparative Study)
Comparative Study
BACKGROUND
Failure of orthodontic bracket bonds is a common occurrence during orthodontic treatment. This study investigated the impact of Er: YAG laser-based removal of adhesive from the bases of metal and ceramic brackets for re-bonding.
METHODS
A total of 168 extracted premolars were collected from patients. 84 metal brackets were used to be bonded on the buccal surface of the premolars in Groups 1, 2, 3 and 4, while 84 ceramic brackets were applied in Groups I, II, III and IV. Group 1/I represented the initial bonding group, with Group 2/II being the re-bonding group with new brackets, while Groups 3/III and 4/ IV received recycled brackets treated by Er: YAG laser or flaming respectively. Both the first and second de-bonding were performed in all samples using a universal testing machine to determine the shear bond strength (SBS). The adhesive remnant index (ARI) was evaluated using a stereo-microscope. The new and the treated bracket bases were evaluated using scanning electron microscopy (SEM). Differences in initial bonding and re-bonding ability were analyzed through one-way ANOVAs, and differences in ARI were assessed with the Kruskal-Wallis test.
RESULTS
Greater amounts of adhesive residue were observed on ceramic brackets treated by laser. The SBS values for recycled metal brackets in Group 3 (26.13 MPa) were comparable to Group 1 (23.62 MPa) whereas they differed significantly from Group 4 (12.54 MPa). No significant differences in these values were observed when comparing the 4 groups with ceramic brackets. ARI score in Group 4 (2-3 points) differed significantly from the three other groups (P < 0.05). For Group I, II, III and IV, similar ARI scores were observed (P > 0.05). SEM analysis didn't show apparent damage of bracket bases consisting of either metal or ceramic material treated by Er: YAG laser.
CONCLUSIONS
Er: YAG laser treatment was superior to flame treatment as a means of removing adhesive without damaging the brackets. SBS values and ARI scores following Er: YAG laser treatment were similar to those for new brackets, offering further support for Er: YAG laser treatment as a viable means of recycling debonded brackets.
Topics: Orthodontic Brackets; Lasers, Solid-State; Humans; Dental Bonding; Ceramics; Dental Debonding; Shear Strength; Dental Stress Analysis; Microscopy, Electron, Scanning; Materials Testing; Surface Properties; Bicuspid; Dental Alloys; Resin Cements
PubMed: 38902669
DOI: 10.1186/s12903-024-04504-2 -
Journal of Materials Science. Materials... Jun 2024Orthopedic and dental implant failure continues to be a significant concern due to localized bacterial infections. Previous studies have attempted to improve implant...
Orthopedic and dental implant failure continues to be a significant concern due to localized bacterial infections. Previous studies have attempted to improve implant surfaces by modifying their texture and roughness or coating them with antibiotics to enhance antibacterial properties for implant longevity. However, these approaches have demonstrated limited effectiveness. In this study, we attempted to engineer the titanium (Ti) alloy surface biomimetically at the nanometer scale, inspired by the cicada wing nanostructure using alkaline hydrothermal treatment (AHT) to simultaneously confer antibacterial properties and support the adhesion and proliferation of mammalian cells. The two modified Ti surfaces were developed using a 4 h and 8 h AHT process in 1 N NaOH at 230 °C, followed by a 2-hour post-calcination at 600 °C. We found that the control plates showed a relatively smooth surface, while the treatment groups (4 h & 8 h AHT) displayed nanoflower structures containing randomly distributed nano-spikes. The results demonstrated a statistically significant decrease in the contact angle of the treatment groups, which increased wettability characteristics. The 8 h AHT group exhibited the highest wettability and significant increase in roughness 0.72 ± 0.08 µm (P < 0.05), leading to more osteoblast cell attachment, reduced cytotoxicity effects, and enhanced relative survivability. The alkaline phosphatase activity measured in all different groups indicated that the 8 h AHT group exhibited the highest activity, suggesting that the surface roughness and wettability of the treatment groups may have facilitated cell adhesion and attachment and subsequently increased secretion of extracellular matrix. Overall, the findings indicate that biomimetic nanotextured surfaces created by the AHT process have the potential to be translated as implant coatings to enhance bone regeneration and implant integration.
Topics: Surface Properties; Osteoblasts; Titanium; Animals; Dental Implants; Biomimetic Materials; Wettability; Cell Adhesion; Anti-Bacterial Agents; Materials Testing; Biomimetics; Humans; Cell Proliferation; Alloys; Prostheses and Implants; Coated Materials, Biocompatible; Nanostructures; Cell Survival; Alkaline Phosphatase; Hemiptera; Cell Line
PubMed: 38896291
DOI: 10.1007/s10856-024-06794-y -
Materials (Basel, Switzerland) May 2024The manufacturing of orthodontic archwires made from NiTi alloy has undergone numerous changes from the second half of the last century to modern times. Initially,... (Review)
Review
The manufacturing of orthodontic archwires made from NiTi alloy has undergone numerous changes from the second half of the last century to modern times. Initially, superelastic-active austenitic NiTi alloys were predominant, followed by thermodynamic-active martensitic NiTi alloys, and, finally, the most recent development was graded thermodynamic alloys. These advancements have been the subject of extensive investigation in numerous studies, as they necessitated a deeper understanding of their properties. Furthermore, it is imperative that we validate the information provided by manufacturers regarding these archwires through independent studies. This review evaluates existing studies on the subject with a specific focus on the Bio-active multi-force NiTi archwire, by examining its mechanical, thermal, and physicochemical properties before and after clinical use. This archwire consists primarily of Ni and Ti, with traces of Fe and Cr, which release graduated, biologically tolerable forces which increase in a front-to-back direction and are affected by the temperature of the environment they are in. The review provides information to practicing orthodontists, facilitating informed decisions regarding the selection and use of Bio-active™ archwires for individual patient treatments.
PubMed: 38893867
DOI: 10.3390/ma17112603 -
The Saudi Dental Journal Jun 2024This in vitro study aimed to evaluate the additive manufacturing (AM) of cobalt chromium Co-Cr and titanium Ti alloy clasps for clinical use. After scanning the Ni-Cr...
This in vitro study aimed to evaluate the additive manufacturing (AM) of cobalt chromium Co-Cr and titanium Ti alloy clasps for clinical use. After scanning the Ni-Cr die of the first molar, Akers' clasps were designed using computer-aided design/ computer-aided manufacturing (CAD/CAM). The clasps were manufactured from Co-Cr-W dental alloy and Ti-6Al-4V alloy powder using AM machines. Then, they were divided into two groups. The initial retentive force of the clasps was measured using a universal testing machine. Cyclic loading of the clasps was carried out by a specially designed insertion-removal testing apparatus in wet condition up to 5000 cycles. Retentive force was measured at 1000, 2000, 3000, 4000, and 5000 cycles. Moreover, the intaglio surface of each clasp was scanned using the scanner; and superimposition between the pre- and post-cycling clasp files was performed to evaluate deformation after cyclic loading. The fitting surfaces of retentive clasp tips were examined with a scanning electron microscope (SEM). Finally, it has been found that the initial retentive force for the Co-Cr group was 10.81 ± 0.37 N, and for the Ti group was 5.41 ± 0.18 N. Additionally, during the testing periods, both Co-Cr and Ti clasps continued to lose retentive force within the cycles of placement and removal. This effect was more prominent in the Co-Cr than in the Ti clasps. The distances between pre- and post-cycling in the retentive arm were -0.290 ± 0.11 mm and -0.004 ± 0.01 mm in Co-Cr and Ti alloys, respectively, and in the reciprocal arm were -0.072 ± 0.04 mm and -0.032 ± 0.04 mm in Co-Cr and Ti alloys, respectively. The retentive force required to remove the Ti clasps was found to be significantly lower than those required to dislodge the Co-Cr clasps. Co-Cr and Ti clasps lost significant amounts of retentive force from the initial use to the 3.5-year periods of simulated clinical use.
PubMed: 38883903
DOI: 10.1016/j.sdentj.2024.04.001 -
Ceramic conversion treated titanium implant abutments with gold for enhanced antimicrobial activity.Dental Materials : Official Publication... Jun 2024Peri-implantitis is an inflammatory process around dental implants that is characterised by bone loss that may jeopardize the long-term survival of osseo integrated...
INTRODUCTION
Peri-implantitis is an inflammatory process around dental implants that is characterised by bone loss that may jeopardize the long-term survival of osseo integrated dental implants. The aim of this study was to create a surface coating on titanium abutments that possesses cellular adhesion and anti-microbial properties as a post-implant placement strategy for patients at risk of peri-implantitis.
MATERIALS AND METHODSMETHODS
Titanium alloy Grade V stubs were coated with gold particles and then subjected to ceramic conversion treatment (CCT) at 620 °C for 3, 8 and 80 h. The surface characteristics and chemistry were assessed using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD) analysis. The leaching profile was investigated by inductively coupled plasma mass spectroscopy (ICP-MS) for all groups after 7, 14 and 28 days in contact with distilled water. A scratch test was conducted to assess the adhesion of the gold coating to the underlying titanium discs. Two bacterial species (Staphylococcus aureus (SA) & Fusobacterium nucleatum (FN)) were used to assess the antibacterial behaviour of the coated discs using a direct attachment assay test. The potential changes in surface chemistry by the bacterial species were investigated by grazing angle XRD.
RESULTS
The gold pre-coated titanium discs exhibited good stability of the coating especially after immersion in distilled water and after bacterial colonisation as evident by XRD analysis. Good surface adhesion of the coating was demonstrated for gold treated discs after scratch test analysis, especially titanium, following a 3-hour (3 H) ceramic conversion treatment. All coated discs exhibited significantly improved antimicrobial properties against both tested bacterial species compared to untreated titanium discs.
CONCLUSIONS
Ceramic conversion treated titanium with a pre-deposited gold layer showed improved antimicrobial properties against both SA and FN species than untreated Ti-C discs. Scratch test analysis showed good adherence properties of the coated discs the oxide layer formed is firmly adherent to the underlying titanium substrate, suggesting that this approach may have clinical efficacy for coating implant abutments.
PubMed: 38853104
DOI: 10.1016/j.dental.2024.05.029 -
Materials (Basel, Switzerland) May 2024Chromium- and cobalt-based alloys, as well as chrome-nickel steels, are most used in dental prosthetics. Unfortunately, these alloys, especially nickel-based alloys, can...
Chromium- and cobalt-based alloys, as well as chrome-nickel steels, are most used in dental prosthetics. Unfortunately, these alloys, especially nickel-based alloys, can cause allergic reactions. A disadvantage of these alloys is also insufficient corrosion resistance. To improve the properties of these alloys, amorphous Si (C,N) coatings were deposited on the surfaces of metal specimens. This paper characterizes coatings of silicon carbide nitrides, deposited by the magnetron sputtering method on the surface of nickel-chromium alloys used in dental prosthetics. Depending on the deposition parameters, coatings with varying carbon to nitrogen ratios were obtained. The study analyzed their structure and chemical and phase composition. In addition, a study of surface wettability and surface roughness was performed. Based on the results obtained, it was found that amorphous coatings of Si (C,N) type with thicknesses of 2 to 4.5 µm were obtained. All obtained coatings increase the value of surface free energy. The study showed that Si (C,N)-type films can be used in dental prosthetics as protective coatings.
PubMed: 38793515
DOI: 10.3390/ma17102450 -
Materials (Basel, Switzerland) May 2024The resistance of nickel-titanium endodontic instruments against cyclic fatigue failure remains a significant concern in clinical settings. This study aimed to assess...
The resistance of nickel-titanium endodontic instruments against cyclic fatigue failure remains a significant concern in clinical settings. This study aimed to assess the cyclic fatigue strength of five nickel-titanium rotary systems, while correlating the results with the instruments' geometric and metallurgical characteristics. A total of 250 new instruments (sizes S1/A1, S2/A2, F1/B1, F2/B2, F3/B3) from ProTaper Gold, ProTaper Universal, Premium Taper Gold, Go-Taper Flex, and U-Files systems underwent mechanical testing. Prior to experimental procedures, all instruments were meticulously inspected to identify irregularities that could affect the investigation. Using a stereomicroscope, design characteristics such as the number of spirals, length, spirals per millimeter, and average helical angle of the active blade were determined. The surface finishing characteristics of the instruments were examined using a scanning electron microscope. Differential scanning calorimetry was employed to establish the instruments' phase transformation temperatures, while energy-dispersive X-ray spectroscopy was utilized to analyze the elemental composition of the alloy. The instruments were subjected to cyclic fatigue testing within a stainless steel non-tapered artificial canal featuring a 6 mm radius and 86 degrees of curvature. Appropriate statistical tests were applied to compare groups, considering a significance level of 0.05. The assessed design characteristics varied depending on the instrument type. The least irregular surface finishing was observed in U-Files and Premium Taper Gold files, while the most irregular surface was noted in Go-Taper Flex. All instruments exhibited near-equiatomic proportions of nickel and titanium elements, whereas ProTaper Universal and U-Files instruments demonstrated lower phase transformation temperatures compared to their counterparts. Larger-sized instruments, as well as ProTaper Universal and U-Files, tended to display lower cyclic fatigue strength results. Overall, the design, metallurgical, and cyclic fatigue outcomes varied among instruments and systems. Understanding these outcomes may assist clinicians in making more informed decisions regarding instrument selection.
PubMed: 38793413
DOI: 10.3390/ma17102345 -
Materials (Basel, Switzerland) May 2024The primary focus of the current paper centers on the microstructures and mechanical properties exhibited by a Ti-30Nb-12Zr-5Ta-2Sn-1.25Fe (wt. %) (TNZTSF) alloy that...
The primary focus of the current paper centers on the microstructures and mechanical properties exhibited by a Ti-30Nb-12Zr-5Ta-2Sn-1.25Fe (wt. %) (TNZTSF) alloy that has been produced through an intricate synthesis process comprising cold-crucible induction in levitation, carried out in an atmosphere controlled by argon, and cold-rolling deformation (CR), applying systematic adjustments in the total deformation degree (total applied thickness reduction), spanning from 10% to 60%. The microstructural characteristics of the processed specimens were investigated by SEM and XRD techniques, and the mechanical properties by tensile and microhardness testing. The collected data indicate that the TNZTSF alloy's microstructure, in the as-received condition, consists of a β-Ti phase, which shows polyhedral equiaxed grains with an average grain size close to 82.5 µm. During the cold-deformation processing, the microstructure accommodates the increased applied deformation degree by increasing crystal defects such as sub-grain boundaries, dislocation cells, dislocation lines, and other crystal defects, powerfully affecting the morphological characteristics. The as-received TNZTSF alloy showed both high strength (i.e., ultimate tensile strength close to σ = 705.6 MPa) and high ductility (i.e., elongation to fracture close to ε = 11.1%) properties, and the computed β-Ti phase had the lattice parameter a = 3.304(7) Å and the average lattice microstrain ε = 0.101(3)%, which are drastically influenced by the applied cold deformation, increasing the strength properties and decreasing the ductility properties due to the increased crystal defects density. Applying a deformation degree close to 60% leads to an ultimate tensile strength close to σ = 1192.1 MPa, an elongation to fracture close to ε = 7.9%, and an elastic modulus close to 54.9 GPa, while the computed β-Ti phase lattice parameter becomes a = 3.302(1) Å.
PubMed: 38793379
DOI: 10.3390/ma17102312 -
Journal of Personalized Medicine May 2024As an alternative to regenerative therapies, numerous authors have recently proposed bringing back subperiosteal implants. The aim of the study was to present our...
As an alternative to regenerative therapies, numerous authors have recently proposed bringing back subperiosteal implants. The aim of the study was to present our clinical experience with a subperiosteal jaw implant that needs minimal bone preparation and enables the rapid implantation of prosthetic teeth in edentulous, atrophic alveolar bone. The research included 36 complete or partial edentulous patients (61 subperiostal implants) over a period of 6 years. To create the patient-specific subperiostal implants design, DentalCAD 3.0 Galway software (exocad GmbH, Darmstadt, Germany) was used and fabricated with a Mysint 100 (Sisma S.p.A., Piovene Rocchette, Italy) by titanium alloy powder. The results showed that only 9 of the 36 cases were successful at 6-year follow-up, while 27 cases had complications, including exposure of the metal frame (early or delayed), mobility of the device prior to the first 4-6 months, and late mobility due to recurrent infections and progressive structure exposure; 1 case failed for reasons unrelated to the device. This study indicated that the prudent application of fully customized subperiosteal jaw implants is a dependable alternative for the dental rehabilitation of atrophic edentulous cases that necessitate bone grafts for traditional fixed dental implant solutions.
PubMed: 38793123
DOI: 10.3390/jpm14050541 -
BMC Oral Health May 2024The use of artificial intelligence in the field of health sciences is becoming widespread. It is known that patients benefit from artificial intelligence applications on...
Evaluating the accuracy of Chat Generative Pre-trained Transformer version 4 (ChatGPT-4) responses to United States Food and Drug Administration (FDA) frequently asked questions about dental amalgam.
BACKGROUND
The use of artificial intelligence in the field of health sciences is becoming widespread. It is known that patients benefit from artificial intelligence applications on various health issues, especially after the pandemic period. One of the most important issues in this regard is the accuracy of the information provided by artificial intelligence applications.
OBJECTIVE
The purpose of this study was to the frequently asked questions about dental amalgam, as determined by the United States Food and Drug Administration (FDA), which is one of these information resources, to Chat Generative Pre-trained Transformer version 4 (ChatGPT-4) and to compare the content of the answers given by the application with the answers of the FDA.
METHODS
The questions were directed to ChatGPT-4 on May 8th and May 16th, 2023, and the responses were recorded and compared at the word and meaning levels using ChatGPT. The answers from the FDA webpage were also recorded. The responses were compared for content similarity in "Main Idea", "Quality Analysis", "Common Ideas", and "Inconsistent Ideas" between ChatGPT-4's responses and FDA's responses.
RESULTS
ChatGPT-4 provided similar responses at one-week intervals. In comparison with FDA guidance, it provided answers with similar information content to frequently asked questions. However, although there were some similarities in the general aspects of the recommendation regarding amalgam removal in the question, the two texts are not the same, and they offered different perspectives on the replacement of fillings.
CONCLUSIONS
The findings of this study indicate that ChatGPT-4, an artificial intelligence based application, encompasses current and accurate information regarding dental amalgam and its removal, providing it to individuals seeking access to such information. Nevertheless, we believe that numerous studies are required to assess the validity and reliability of ChatGPT-4 across diverse subjects.
Topics: Dental Amalgam; United States; United States Food and Drug Administration; Humans; Artificial Intelligence; Surveys and Questionnaires
PubMed: 38789962
DOI: 10.1186/s12903-024-04358-8