Medicina (Kaunas, Lithuania) Dec 2022: Porcelain-fused-to-metal (PFM) prostheses are considered the gold standard for the replacement of missing teeth, however, these have several drawbacks. Therefore,... (Review)
Review
: Porcelain-fused-to-metal (PFM) prostheses are considered the gold standard for the replacement of missing teeth, however, these have several drawbacks. Therefore, lithium disilicate (LDS) prostheses have been introduced for the construction of fixed crowns and bridges. The aim of this systematic review was to ascertain the long-term survival of LDS fixed prostheses in comparison to other materials. : The focused question was 'In patients who have undergone prosthodontic treatment (participants), what are the overall survival rate of lithium disilicate (LDS) crowns and fixed bridges; and how do they relate to survival rates of non-LDS similar restoration are the survival and com-plication rates (outcomes) of LDS-based fixed prostheses with complete coverage (intervention) higher or lower when compared to non-LDS materials (controls)?'. An electronic search was conducted in PubMED/Medline, EMBASE, Google Scholar, and ClinicalTrials.gov for articles published between January 2006 and August 2022 using appropriate MeSH terms and keywords. The following types of studies were included: (1) All types of prospective clinical studies; (2) Clinical studies focusing on the survival of fixed LDS bridges and crowns; (3) Studies using natural teeth with complete coverage as abutment for fixed LDS bridges and crowns; and (4) Studies in English. The following studies were excluded: (1) Laboratory/in vitro studies and studies on LDS prostheses with no description of outcomes or survival rates; (2) Commentaries; (3) Letters to the editor; (4) Reviews; and (5) Internal data from manufacturers. The data from included studies were extracted and the risk of bias was assessed within the studies using ROBINS-I. : A total of 25 studies were included in this systematic review. The overall 5-year and 10-year survival rates were of 95-100% and 71.4-100%, respectively. Generally, three-unit bridges had a significantly lower survival rate over 5 and 10 years compared to single-unit crowns. Overall, the risk of bias in the included studies was moderate. : The LDS-based complete coverage prostheses have a survival rate ranging between 48.6% and 100%. Furthermore, due to the lack of comparative studies, the long-term function and survival of LDS prostheses compared to other material prosthesis (PFM and ZrO) is debatable.
Topics: Humans; Dental Porcelain; Prospective Studies; Crowns; Metals
PubMed: 36676719
DOI: 10.3390/medicina59010095 -
Journal of the Mechanical Behavior of... Feb 2023The present systematic review and meta-analysis aimed to assess the characteristics and consequences of post-processing methods after grinding procedures in YSZ ceramics... (Meta-Analysis)
Meta-Analysis Review
The present systematic review and meta-analysis aimed to assess the characteristics and consequences of post-processing methods after grinding procedures in YSZ ceramics on its surface roughness and flexural strength. The protocol of this review was made prospectively and is available online in the PROSPERO database (link). Literature searches on PubMed/MEDLINE, EMBASE, Lilacs, Web of Science and Scopus were conducted on December 2022 to select in vitro studies written in English, without publishing-date restrictions, that considered surface characteristics and mechanical properties of YSZ ceramics submitted to grinding and subsequent post-processing surface treatments as an attempt to revert the effect induced by grinding. Two authors independently selected the studies, extracted the data and assessed the risk of bias. Mean differences (Rev-Man 5.1, random effects model, α= 0.05) were obtained by comparing flexural strength and surface roughness values of ground surfaces with at least one post-processing surface treatment (global analysis). Subgroup analyses were performed considering the most prevalent categories of post-processing methods. A total of 33 (out of 4032) studies were eligible and included in the analysis. In the global analysis, ground surfaces showed higher flexural strength than when post-processing methodologies were employed (p< 0.0001). The subgroup analysis showed that only polishing was able to enhance the flexural strength after grinding (p= 0.001); however, when other protocols were used, the ground surface was always superior in terms of flexural strength (p< 0.0001). Post-processing techniques in both the global and sub-group analyses were able to reduce the surface roughness after grinding in YSZ ceramics (p< 0.00001). High heterogeneity was found in all the meta-analyses. Concerning the risk of bias analysis, the included studies had mixed scores for the considered factors. In conclusion, in terms of improving flexural strength and restoring surface roughness after grinding, polishing protocols can be considered the best indication as post-processing treatment after YSZ ceramics adjustments/grinding.
Topics: Humans; Materials Testing; Surface Properties; Zirconium; Yttrium; Ceramics; Dental Polishing; Dental Porcelain
PubMed: 36634437
DOI: 10.1016/j.jmbbm.2023.105654 -
Dental Research Journal 2022It is a major concern to select a proper ceramic with acceptable strength and esthetic and minimum antagonist wear. Therefore, different ceramics were introduced to... (Review)
Review
It is a major concern to select a proper ceramic with acceptable strength and esthetic and minimum antagonist wear. Therefore, different ceramics were introduced to obtain these advantages with various surface treatments. The aim of this study is to evaluate and report the wear behavior of polished and glazed feldspathic and zirconia crowns in published articles up to 2020. Five electronic databases which were used in this research were MEDLINE (via PubMed), Web of Science, Cochrane Library, Embase, and Scopus from the starting date of databases to January 2020. The Keywords "zirconia," "feldspathic," "dental ceramic," "enamel," "Y-TZP," "wear," "glazed," and "polished" were used. English articles were selected in this paper. The Preferred Reporting Items for Systematic Reviews and Meta-Analyses statement was used as a reporting template as much as possible. Among the initially 133 articles, 59 duplicated articles were removed, and finally, 52 articles were screened and among them, only 16 articles remained for full-text regaining. The results showed that zirconia had significantly less antagonist wear than feldspathic groups, and polishing had less enamel wear than other types of surface treatment like glazing. Only one study showed that glazed zirconia can have more antagonist wear than feldspathic porcelain. Monolithic zirconia had less enamel wear than conventional zirconia and low-fusing feldspathic porcelain showed lower antagonist wear in comparing with other types of feldspathic porcelains.
PubMed: 36605138
DOI: No ID Found -
Cureus Nov 2022This study aimed to systematically review the literature to evaluate the marginal adaptation of veneers using different fabrication methods, namely, conventional... (Review)
Review
This study aimed to systematically review the literature to evaluate the marginal adaptation of veneers using different fabrication methods, namely, conventional feldspathic porcelain laminate veneers (PLVs), computer-aided design-computer-aided machining (CAD-CAM) veneers, and pressed veneers. A comprehensive literature search was performed using electronic databases (PubMed and Google Scholar) as well as hand searches to identify all relevant studies related to veneers and marginal adaptation. The identified studies were screened for assessing the inclusion and exclusion criteria. The included articles were then subjected to data extraction and analysis. The search resulted in 130 articles, of which six were included in this systematic review. All included articles were assessed for adaptation of margins. Based on the findings of this systematic review, no significant differences were found in the marginal adaptation of CAD-CAM and conventional feldspathic PLVs. The marginal fidelity of ceramic veneers issuing from the various fabrication techniques was clinically acceptable.
PubMed: 36579272
DOI: 10.7759/cureus.31885 -
The Journal of Prosthetic Dentistry Jun 2024Computer-aided design and computer-aided manufacturing (CAD-CAM) blocks have evolved rapidly, making it difficult to establish the best clinical protocol for bonding a... (Meta-Analysis)
Meta-Analysis Review
STATEMENT OF PROBLEM
Computer-aided design and computer-aided manufacturing (CAD-CAM) blocks have evolved rapidly, making it difficult to establish the best clinical protocol for bonding a given block and whether an established protocol is appropriate for a newly introduced product.
PURPOSE
This integrative systematic review and meta-analysis aimed to clarify whether the clinician can select the most efficient adhesion protocols for CAD-CAM blocks by reading published in vitro studies and implementing them in daily practice.
MATERIAL AND METHODS
Based on the population, intervention, comparison, and outcome (PICO) strategy, 3 databases were searched for in vitro studies, randomized clinical trials, prospective or retrospective studies, and case reports from January 1, 2015, to July 31, 2021. A meta-analysis analyzed 28 studies to calculate the mean difference between best and worst protocols for each author and block with a random-effects model (α=.05).
RESULTS
From 508 relevant studies, 37 in vitro studies, 2 clinical studies, and 1 clinical report were selected for data extraction and qualitative analysis. Vita Enamic, IPS e.max CAD, LAVA Ultimate, and Vita Mark II blocks were the most studied, and RelyX Ultimate was the most used luting cement. The meta-analysis confirmed the null hypothesis that the evidence-based efficacy of clinical protocols to bond CAD-CAM blocks is still controversial (P<.05).
CONCLUSIONS
There are objective standards for individual in vitro tests, but the studies lack standardization. Some tested protocols were more efficient than others. Randomized clinical trials and well-documented clinical situations were almost nonexistent, making direct application of in vitro findings in clinical practice impossible.
Topics: Computer-Aided Design; Humans; Dental Bonding; Clinical Protocols; Dental Porcelain; In Vitro Techniques; Ceramics
PubMed: 36543700
DOI: 10.1016/j.prosdent.2022.08.024 -
Primary Dental Journal Dec 2022The purpose of this systematic review was to compare the clinical performance of lithium disilicate (LDS) and zirconia (Z) single crowns manufactured by computer-aided...
PURPOSE
The purpose of this systematic review was to compare the clinical performance of lithium disilicate (LDS) and zirconia (Z) single crowns manufactured by computer-aided design/computer-aided manufacturing (CAD/CAM) systems using intraoral optical scanners (IOS).
MATERIALS AND METHODS
An electronic search for articles published between January 2012 and January 2022 in the English language was performed with the Medline/Pubmed database under the guidelines of Preferred Reporting Items for Systemic Reviews and Meta-analysis (PRISMA). The specific search terms used were "zirconia", "lithium disilicate", "CAD/CAM", "intraoral optical scanner", and "survival".
RESULTS
The initial electronic search resulted in 278 articles. Most of the resulting articles were excluded, six clinical studies addressing the clinical outcomes of Z and LDS crowns fitted the inclusion criteria and were selected for review. Of these six studies, three were randomised controlled trials, two were retrospective studies, and one was a prospective study. To quantify the clinical performance of the crowns several parameters were recorded, including fractures, endodontic complications, periodontal complications, technical complications, aesthetic complications, and biological complications. It was noted that the most common technical complication of Z and LDS crowns was chipping at a rate of 1.4% and 5% respectively. Regarding Z crowns, aesthetic concerns were the most frequently observed complication.
CONCLUSION
The outcomes of this systematic review indicate that Z and LDS crowns display a similar incidence of periodontal and endodontic complications when compared to metal-ceramic crowns, suggesting that these all-ceramic materials are viable alternatives. The incidence of chipping was higher in LDS crowns compared to other materials, while Z crowns were inferior in terms of aesthetics.
Topics: Humans; Ceramics; Computer-Aided Design; Crowns; Dental Porcelain; Dental Prosthesis Design; Lithium; Prospective Studies; Randomized Controlled Trials as Topic; Retrospective Studies; Zirconium
PubMed: 36533368
DOI: 10.1177/20501684221132941 -
Cureus Oct 2022The prosthesis must have good survival despite being functional for at least 5-10 years. This makes sure that the replacement of missing teeth does not become a repeated... (Review)
Review
The prosthesis must have good survival despite being functional for at least 5-10 years. This makes sure that the replacement of missing teeth does not become a repeated expense. Of 579 identified articles, 15 met the inclusion criteria for systematic review. Missing teeth replacement materials are divided into two groups: porcelain fused to metal and all ceramics. Data related to survival rates as well as the most common mode of failure is observed from both groups. It was observed that porcelain fused to metal prostheses had an approximately 99.5% survival rate and an approximately 92% survival rate for all-ceramic tooth-supported prostheses after five years of insertion. Porcelain-fused-to-metal (PFM) prostheses had a better survival rate after five years of insertion as compared to all-ceramic prostheses. Porcelain fused to metal should be the treatment of choice for dentists and patients when missing teeth need to be fixed.
PubMed: 36407172
DOI: 10.7759/cureus.30338 -
Journal of Clinical Medicine Nov 2022This systematic review and meta-analysis aimed to evaluate the wear of the antagonist tooth in ceramic restorations. (Review)
Review
BACKGROUND
This systematic review and meta-analysis aimed to evaluate the wear of the antagonist tooth in ceramic restorations.
MATERIAL AND METHODS
This study was carried out based on Preferred Reporting Items for Systematic Review and Meta-analysis (PRISMA) recommendations; it was also registered in PROSPERO (register number: CRD42022316252). Three databases were consulted in the literature search, Embase, Scopus, and Web of Science. The citation searching was conducted by two researchers independently. The clinical studies that evaluated wear in antagonist teeth concerning ceramic restoration were included. Twelve articles were selected after eliminating duplicates ones and applying the inclusion criteria, and two were chosen through citation. Fourteen articles were considered for the qualitative and quantitative analysis (meta-regression and meta-analysis).
RESULTS
The mean linear wear of the antagonist tooth in relation to feldspathic was 8.914 μm, for lithium disilicate it was 0.018 μm, and for zirconia it was 0.257 μm. The mean volumetric wear of the antagonist tooth in relation to feldspathic was 0.273 mm, for hybrid ceramic it was 0.030 mm, for lithium disilicate it was 0.018 mm, and for zirconia it was 0.014 mm. The mean natural tooth wear was 0.7974 μm per month. Tooth wear caused by zirconia at six months was 31.755 μm, at 12 months it was 24.648 μm, and at 24 months it was 20.662 μm.
CONCLUSIONS
Feldspathic produces greater wear of the antagonist tooth from ceramic restorations linearly and volumetrically. In addition, zirconia generates the least wear that will decrease over time, and it will be equal to or less than the natural wear in the tooth.
PubMed: 36362777
DOI: 10.3390/jcm11216547 -
European Journal of Oral Sciences Dec 2022Advances of digital technology are rapidly adopted in dental practice. This systematic review aimed to collect evidence on the accuracy of fit of different types of... (Review)
Review
Advances of digital technology are rapidly adopted in dental practice. This systematic review aimed to collect evidence on the accuracy of fit of different types of fixed dental prostheses (FDPs) fabricated through digital, conventional, or combination impression techniques. Data collection was based on the guidelines of the preferred reporting items for systematic reviews and meta-analyses (PRISMA). Two databases (PubMed, Scopus) were searched for articles in English published between 2010 and 2021 resulting in 480 articles. Of those, 35 studies fulfilled the inclusion criteria. These articles referred to three groups of materials/techniques including all-ceramic (zirconia; lithium disilicate) and porcelain-fused-to-metal (PFM) restorations. Results showed clinically acceptable marginal fit (< 120 μm) for all materials and impression techniques. Α fully digital workflow appears more promising for the construction of short-span zirconia FDPs. Nevertheless, most articles evaluated marginal/internal fit of single crowns or short-span FDPs in vitro, while clinical data are limited for long-span FDPs. The necessity for gingival retraction remains a major drawback of all impression techniques, increasing procedural time and patient discomfort. Besides, factors related to the fabrication process, including milling and 3D printing of working models significantly influence the outcome. Overall, there still some way to go before digital technology can be incorporated in complex treatment plans in prosthodontics.
Topics: Humans; Dental Prosthesis; Dental Restoration, Permanent
PubMed: 36346664
DOI: 10.1111/eos.12902 -
Journal of Conservative Dentistry : JCD 2022Advances in adhesive technologies and escalation in esthetic demands have increased indications for tooth-colored, partial coverage restorations. Recently, material... (Review)
Review
BACKGROUND
Advances in adhesive technologies and escalation in esthetic demands have increased indications for tooth-colored, partial coverage restorations. Recently, material knowledge has evolved, new materials have been developed, and no systematic review has answered the question posed by practitioners: Is the clinical efficacy of resin or ceramic better, for inlay, onlay, and overlay in the long run?
AIM
The aim of this systematic review and meta-analysis was to evaluate the clinical performance of ceramic and resin inlays, onlays, and overlays and to identify the complication types associated with the main clinical outcomes.
MATERIALS AND METHODS
Two reviewers (VN and AJ) searched PubMed, Embase, and Cochrane Central registry of controlled trials for published articles between 1983 and 2020 conforming to Preferred Reporting Items for Systematic Reviews and Meta-analyses guidelines for systematic reviews. Only clinical studies which met the following criteria were included (1) studies regarding ceramic and resin inlays, onlays, and overlays were included; (2) randomized controlled trials, retrospective or prospective studies conducted in humans; (3) studies with a dropout rate <50% 4) studies with a follow-up higher than 5 years.
RESULTS
Of 1718 articles, 21 articles were selected. At 5 years, the estimated survival rates for resin ( = 129) was 86%, feldspathic porcelain ( = 1048) was 90%, and glass ceramic ( = 2218) was 92%; at 10 years, the survival of resin was 75% ( = 115), feldspathic porcelain was 91% ( = 1829), and glass ceramic was 89% ( = 1075).
CONCLUSION
The meta-regression indicated that ceramic partial coverage restorations (feldspathic porcelain and glass-ceramic) outperformed resin partial coverage restorations both at 5-year and 10-year follow-up. When compared between ceramic types, glass ceramics outperformed feldspathic porcelain at 5 years' follow-up and feldspathic porcelain outperformed glass ceramics at 10 years' follow-up. The failures were mostly due to fractures (6.2%), endodontic problems (3%), secondary caries (1.7%), and debonding which was 0.9%.
PubMed: 36187858
DOI: 10.4103/jcd.jcd_184_22