Dental Research Journal 2023The aim of the current study was to evaluate the outcomes and complications of three-unit porcelain-fused-to-metal tooth-implant-supported prostheses in comparison with... (Review)
Review
Comparison of the outcomes and complications of three-unit porcelain-fused-to-metal tooth-implant-supported prostheses with implant-supported prostheses: A systematic review and meta-analysis.
BACKGROUND
The aim of the current study was to evaluate the outcomes and complications of three-unit porcelain-fused-to-metal tooth-implant-supported prostheses in comparison with implant-supported prostheses.
MATERIALS AND METHODS
In this review article, the electronic databases, PubMed, Scopus, LILACS, Web of Science, EBSCO, LIVIVO, and Embase were searched over the past 20 years until December 2021. Risk ratio with 95% confidence interval (CI), fixed effect model, and Mantel-Haenszel method was calculated. The meta-analysis was performed with the statistical software Stata/MP v. 16.
RESULTS
Two hundred and three studies were selected for reviewing the abstracts, from which the full texts of 16 studies were reviewed. Finally, five studies were selected. The risk ratio of prosthesis failure between the tooth-implant-supported prosthesis and the implant-supported prosthesis was RR (Risk Ratio)= 1.83 (0.79, 4.24), ( = 0.16) and for prosthesis complication, it was RR = 0.61 (0.35, 1.06), ( = 0.08). Risk ratio of implant failure between the mentioned groups was RR = 2.33 (0.84, 6.41), ( = 0.10), and for implant complications, this rate was 0.09 (RR, 0.09 95% CI - 1.30, 1.48; = 0.90).
CONCLUSION
The meta-analysis of the present study showed that there was no significant difference between the two groups (three-unit porcelain-fused-to-metal tooth-implant-supported prosthesis and implant-supported prosthesis reconstruction) in terms of the total failure of implants and prostheses and the complication rate of implants and prostheses.
PubMed: 36820133
DOI: No ID Found -
Medicina (Kaunas, Lithuania) Dec 2022: Porcelain-fused-to-metal (PFM) prostheses are considered the gold standard for the replacement of missing teeth, however, these have several drawbacks. Therefore,... (Review)
Review
: Porcelain-fused-to-metal (PFM) prostheses are considered the gold standard for the replacement of missing teeth, however, these have several drawbacks. Therefore, lithium disilicate (LDS) prostheses have been introduced for the construction of fixed crowns and bridges. The aim of this systematic review was to ascertain the long-term survival of LDS fixed prostheses in comparison to other materials. : The focused question was 'In patients who have undergone prosthodontic treatment (participants), what are the overall survival rate of lithium disilicate (LDS) crowns and fixed bridges; and how do they relate to survival rates of non-LDS similar restoration are the survival and com-plication rates (outcomes) of LDS-based fixed prostheses with complete coverage (intervention) higher or lower when compared to non-LDS materials (controls)?'. An electronic search was conducted in PubMED/Medline, EMBASE, Google Scholar, and ClinicalTrials.gov for articles published between January 2006 and August 2022 using appropriate MeSH terms and keywords. The following types of studies were included: (1) All types of prospective clinical studies; (2) Clinical studies focusing on the survival of fixed LDS bridges and crowns; (3) Studies using natural teeth with complete coverage as abutment for fixed LDS bridges and crowns; and (4) Studies in English. The following studies were excluded: (1) Laboratory/in vitro studies and studies on LDS prostheses with no description of outcomes or survival rates; (2) Commentaries; (3) Letters to the editor; (4) Reviews; and (5) Internal data from manufacturers. The data from included studies were extracted and the risk of bias was assessed within the studies using ROBINS-I. : A total of 25 studies were included in this systematic review. The overall 5-year and 10-year survival rates were of 95-100% and 71.4-100%, respectively. Generally, three-unit bridges had a significantly lower survival rate over 5 and 10 years compared to single-unit crowns. Overall, the risk of bias in the included studies was moderate. : The LDS-based complete coverage prostheses have a survival rate ranging between 48.6% and 100%. Furthermore, due to the lack of comparative studies, the long-term function and survival of LDS prostheses compared to other material prosthesis (PFM and ZrO) is debatable.
Topics: Humans; Dental Porcelain; Prospective Studies; Crowns; Metals
PubMed: 36676719
DOI: 10.3390/medicina59010095 -
Dental Research Journal 2022It is a major concern to select a proper ceramic with acceptable strength and esthetic and minimum antagonist wear. Therefore, different ceramics were introduced to... (Review)
Review
It is a major concern to select a proper ceramic with acceptable strength and esthetic and minimum antagonist wear. Therefore, different ceramics were introduced to obtain these advantages with various surface treatments. The aim of this study is to evaluate and report the wear behavior of polished and glazed feldspathic and zirconia crowns in published articles up to 2020. Five electronic databases which were used in this research were MEDLINE (via PubMed), Web of Science, Cochrane Library, Embase, and Scopus from the starting date of databases to January 2020. The Keywords "zirconia," "feldspathic," "dental ceramic," "enamel," "Y-TZP," "wear," "glazed," and "polished" were used. English articles were selected in this paper. The Preferred Reporting Items for Systematic Reviews and Meta-Analyses statement was used as a reporting template as much as possible. Among the initially 133 articles, 59 duplicated articles were removed, and finally, 52 articles were screened and among them, only 16 articles remained for full-text regaining. The results showed that zirconia had significantly less antagonist wear than feldspathic groups, and polishing had less enamel wear than other types of surface treatment like glazing. Only one study showed that glazed zirconia can have more antagonist wear than feldspathic porcelain. Monolithic zirconia had less enamel wear than conventional zirconia and low-fusing feldspathic porcelain showed lower antagonist wear in comparing with other types of feldspathic porcelains.
PubMed: 36605138
DOI: No ID Found -
Cureus Nov 2022This study aimed to systematically review the literature to evaluate the marginal adaptation of veneers using different fabrication methods, namely, conventional... (Review)
Review
This study aimed to systematically review the literature to evaluate the marginal adaptation of veneers using different fabrication methods, namely, conventional feldspathic porcelain laminate veneers (PLVs), computer-aided design-computer-aided machining (CAD-CAM) veneers, and pressed veneers. A comprehensive literature search was performed using electronic databases (PubMed and Google Scholar) as well as hand searches to identify all relevant studies related to veneers and marginal adaptation. The identified studies were screened for assessing the inclusion and exclusion criteria. The included articles were then subjected to data extraction and analysis. The search resulted in 130 articles, of which six were included in this systematic review. All included articles were assessed for adaptation of margins. Based on the findings of this systematic review, no significant differences were found in the marginal adaptation of CAD-CAM and conventional feldspathic PLVs. The marginal fidelity of ceramic veneers issuing from the various fabrication techniques was clinically acceptable.
PubMed: 36579272
DOI: 10.7759/cureus.31885 -
The Journal of Prosthetic Dentistry Jun 2024Computer-aided design and computer-aided manufacturing (CAD-CAM) blocks have evolved rapidly, making it difficult to establish the best clinical protocol for bonding a... (Meta-Analysis)
Meta-Analysis Review
STATEMENT OF PROBLEM
Computer-aided design and computer-aided manufacturing (CAD-CAM) blocks have evolved rapidly, making it difficult to establish the best clinical protocol for bonding a given block and whether an established protocol is appropriate for a newly introduced product.
PURPOSE
This integrative systematic review and meta-analysis aimed to clarify whether the clinician can select the most efficient adhesion protocols for CAD-CAM blocks by reading published in vitro studies and implementing them in daily practice.
MATERIAL AND METHODS
Based on the population, intervention, comparison, and outcome (PICO) strategy, 3 databases were searched for in vitro studies, randomized clinical trials, prospective or retrospective studies, and case reports from January 1, 2015, to July 31, 2021. A meta-analysis analyzed 28 studies to calculate the mean difference between best and worst protocols for each author and block with a random-effects model (α=.05).
RESULTS
From 508 relevant studies, 37 in vitro studies, 2 clinical studies, and 1 clinical report were selected for data extraction and qualitative analysis. Vita Enamic, IPS e.max CAD, LAVA Ultimate, and Vita Mark II blocks were the most studied, and RelyX Ultimate was the most used luting cement. The meta-analysis confirmed the null hypothesis that the evidence-based efficacy of clinical protocols to bond CAD-CAM blocks is still controversial (P<.05).
CONCLUSIONS
There are objective standards for individual in vitro tests, but the studies lack standardization. Some tested protocols were more efficient than others. Randomized clinical trials and well-documented clinical situations were almost nonexistent, making direct application of in vitro findings in clinical practice impossible.
Topics: Computer-Aided Design; Humans; Dental Bonding; Clinical Protocols; Dental Porcelain; In Vitro Techniques; Ceramics
PubMed: 36543700
DOI: 10.1016/j.prosdent.2022.08.024 -
Cureus Oct 2022The prosthesis must have good survival despite being functional for at least 5-10 years. This makes sure that the replacement of missing teeth does not become a repeated... (Review)
Review
The prosthesis must have good survival despite being functional for at least 5-10 years. This makes sure that the replacement of missing teeth does not become a repeated expense. Of 579 identified articles, 15 met the inclusion criteria for systematic review. Missing teeth replacement materials are divided into two groups: porcelain fused to metal and all ceramics. Data related to survival rates as well as the most common mode of failure is observed from both groups. It was observed that porcelain fused to metal prostheses had an approximately 99.5% survival rate and an approximately 92% survival rate for all-ceramic tooth-supported prostheses after five years of insertion. Porcelain-fused-to-metal (PFM) prostheses had a better survival rate after five years of insertion as compared to all-ceramic prostheses. Porcelain fused to metal should be the treatment of choice for dentists and patients when missing teeth need to be fixed.
PubMed: 36407172
DOI: 10.7759/cureus.30338 -
Journal of Clinical Medicine Nov 2022This systematic review and meta-analysis aimed to evaluate the wear of the antagonist tooth in ceramic restorations. (Review)
Review
BACKGROUND
This systematic review and meta-analysis aimed to evaluate the wear of the antagonist tooth in ceramic restorations.
MATERIAL AND METHODS
This study was carried out based on Preferred Reporting Items for Systematic Review and Meta-analysis (PRISMA) recommendations; it was also registered in PROSPERO (register number: CRD42022316252). Three databases were consulted in the literature search, Embase, Scopus, and Web of Science. The citation searching was conducted by two researchers independently. The clinical studies that evaluated wear in antagonist teeth concerning ceramic restoration were included. Twelve articles were selected after eliminating duplicates ones and applying the inclusion criteria, and two were chosen through citation. Fourteen articles were considered for the qualitative and quantitative analysis (meta-regression and meta-analysis).
RESULTS
The mean linear wear of the antagonist tooth in relation to feldspathic was 8.914 μm, for lithium disilicate it was 0.018 μm, and for zirconia it was 0.257 μm. The mean volumetric wear of the antagonist tooth in relation to feldspathic was 0.273 mm, for hybrid ceramic it was 0.030 mm, for lithium disilicate it was 0.018 mm, and for zirconia it was 0.014 mm. The mean natural tooth wear was 0.7974 μm per month. Tooth wear caused by zirconia at six months was 31.755 μm, at 12 months it was 24.648 μm, and at 24 months it was 20.662 μm.
CONCLUSIONS
Feldspathic produces greater wear of the antagonist tooth from ceramic restorations linearly and volumetrically. In addition, zirconia generates the least wear that will decrease over time, and it will be equal to or less than the natural wear in the tooth.
PubMed: 36362777
DOI: 10.3390/jcm11216547 -
Journal of Conservative Dentistry : JCD 2022Advances in adhesive technologies and escalation in esthetic demands have increased indications for tooth-colored, partial coverage restorations. Recently, material... (Review)
Review
BACKGROUND
Advances in adhesive technologies and escalation in esthetic demands have increased indications for tooth-colored, partial coverage restorations. Recently, material knowledge has evolved, new materials have been developed, and no systematic review has answered the question posed by practitioners: Is the clinical efficacy of resin or ceramic better, for inlay, onlay, and overlay in the long run?
AIM
The aim of this systematic review and meta-analysis was to evaluate the clinical performance of ceramic and resin inlays, onlays, and overlays and to identify the complication types associated with the main clinical outcomes.
MATERIALS AND METHODS
Two reviewers (VN and AJ) searched PubMed, Embase, and Cochrane Central registry of controlled trials for published articles between 1983 and 2020 conforming to Preferred Reporting Items for Systematic Reviews and Meta-analyses guidelines for systematic reviews. Only clinical studies which met the following criteria were included (1) studies regarding ceramic and resin inlays, onlays, and overlays were included; (2) randomized controlled trials, retrospective or prospective studies conducted in humans; (3) studies with a dropout rate <50% 4) studies with a follow-up higher than 5 years.
RESULTS
Of 1718 articles, 21 articles were selected. At 5 years, the estimated survival rates for resin ( = 129) was 86%, feldspathic porcelain ( = 1048) was 90%, and glass ceramic ( = 2218) was 92%; at 10 years, the survival of resin was 75% ( = 115), feldspathic porcelain was 91% ( = 1829), and glass ceramic was 89% ( = 1075).
CONCLUSION
The meta-regression indicated that ceramic partial coverage restorations (feldspathic porcelain and glass-ceramic) outperformed resin partial coverage restorations both at 5-year and 10-year follow-up. When compared between ceramic types, glass ceramics outperformed feldspathic porcelain at 5 years' follow-up and feldspathic porcelain outperformed glass ceramics at 10 years' follow-up. The failures were mostly due to fractures (6.2%), endodontic problems (3%), secondary caries (1.7%), and debonding which was 0.9%.
PubMed: 36187858
DOI: 10.4103/jcd.jcd_184_22 -
Journal of Clinical and Experimental... Sep 2022Evaluation of the different causes listed in literature for the rate of success of Zirconia based restorations. (Review)
Review
BACKGROUND
Evaluation of the different causes listed in literature for the rate of success of Zirconia based restorations.
MATERIAL AND METHODS
With the help of PRISMA guidelines , this Systematic review was carried out. For a time span of 18 years that is from 2003 to 2020, articles were searched using three electronic data bases which are PubMed , Cochrane Library and Sciencedirect. The selected 27 articles which included the in vivo as well as the in vitro studies presented the performance of zirconia-based prosthetic restorations. The studies also stated the commonest reason for failure which ultimately depicted the rate of success of the fixed dental prosthesis. Due to heterogeneity of gathered information , meta analysis could not be carried out.
RESULTS
Failure of bond between veneer material and zirconia sub-structure could be related to the cause of fracture of veneering porcelain hypothetically.
CONCLUSIONS
Mechanical connection and building up of compressive strength due to thermal contraction at the time of cooling after sintering process is the reason for the bond developed amongst the two materials. Zirconia based restorations, zirconia failure cause.
PubMed: 36158774
DOI: 10.4317/jced.59711 -
Clinical and Experimental Dental... Dec 2022This systematic review aims to investigate the effect of different preparation designs on the marginal fit and fracture strength of ceramic occlusal veneers. (Review)
Review
OBJECTIVES
This systematic review aims to investigate the effect of different preparation designs on the marginal fit and fracture strength of ceramic occlusal veneers.
MATERIALS AND METHODS
Based on the PICO question and the search terms, an electronic search was performed in Google Scholar, PubMed (MEDLINE), Scopus, Cochrane Library, Web of Science, Science Direct, Wiley, Ovid, and SAGE for articles published up to July 2022. After including English in vitro studies that evaluated posterior ceramic occlusal overlays at the posterior with ceramic restorations by following the PRISMA statement, the extracted data was tabulated. The methodological quality of the included studies was evaluated. Risk of bias assessment was done independently by two authors using the modified MINORS scale.
RESULTS
About 3138 search results were screened, of which 22 were selected due to their titles. Twenty-one full-text articles were assessed for eligibility. Seventeen in-vitro studies were finalized for the extraction of quantitative data. All 17 articles had a low risk of bias and were retained. The influencing items for evaluating the research were different in most studies; therefore, qualitative synthesis of the results was feasible. They generally included preparation design, material thickness, depth of preparation in the tooth, internal divergence angle, and finish line. Meta-analysis was not done due to heterogeneity of preparation types and evaluation methods. Results revealed that fracture resistance of occlusal veneers is higher than normal mastication force, and it is sufficient to prepare the occlusal surface, use a self-etching primer for bonding, and an acceptable minimum ceramic thickness. The marginal discrepancy of occlusal veneers is clinically acceptable. However, this systematic review faces some limitations due to the lack of in vivo studies, different preparation designs in included studies, different follow-ups, and lack of comprehensive explanations in articles.
CONCLUSIONS
The preparation design of occlusal veneers influences both marginal adaptation and fracture resistance. Various preparation designs are proven to have clinically acceptable fracture strength and marginal adaptation.
Topics: Dental Porcelain; Dental Veneers; Flexural Strength; Dental Stress Analysis; Materials Testing; Ceramics
PubMed: 36062841
DOI: 10.1002/cre2.653