Materials (Basel, Switzerland) Jun 2024Direct scanning of silicone impressions is a valid technique. However, studies in implant-supported rehabilitations are lacking. This in vitro study aims to compare the...
Direct scanning of silicone impressions is a valid technique. However, studies in implant-supported rehabilitations are lacking. This in vitro study aims to compare the trueness of impressions obtained with two types of silicone and their corresponding stone casts, using two laboratory scanners in a full-arch implant rehabilitation. A master cast with six dental implants was scanned with a 12-megapixel scanner to obtain a digital master cast. Ten implant impressions were made using two silicones (Zhermack and Coltene) with the open-tray technique. The impressions and stone casts were scanned by two extraoral scanners (Identica T500, Medit; and S600 ARTI, Zirkonzhan). Trueness was assessed by comparing linear and angular distances in digital casts with the master cast. A < 0.05 significance level was considered. The results showed that for the linear measurements, 72% were higher than the master cast measurements, and no consistent pattern was observed in the angular measurements. The greatest deviations were detected between the most posterior implants, with mean values ranging between 173 and 314 µm. No significant differences were found between scanners. However, differences were observed in the distances between silicones (46.7%) and between impressions and stone casts (73.3%). This work demonstrates that the direct scanning of silicone impressions yields results comparable to those obtained from scanning gypsum casts in full-arch implant-supported rehabilitation.
PubMed: 38930301
DOI: 10.3390/ma17122932 -
General Dentistry 2024Patients are always looking for conservative, esthetic, and long-lasting dental restorations, and the technique used directly influences the longevity of the treatment....
Patients are always looking for conservative, esthetic, and long-lasting dental restorations, and the technique used directly influences the longevity of the treatment. The location of the restoration in the mouth and the extent of the decay influence the treatment choice. The larger the dimensions of the cavity preparation, the greater the difficulties in restoring the tooth using direct techniques. The semidirect technique, when indicated, can achieve satisfactory results. It is a relatively easy procedure, consisting of tooth preparation to receive an indirect restoration, fabrication of an alginate impression, fabrication of the composite resin restoration on a flexible cast, cementation, removal of excess cement, and occlusal adjustment. The aim of this case report is to present a viable alternative to direct and indirect restorations for posterior teeth with extensive decay. The article describes the extraoral semidirect technique for fabricating a composite resin restoration, highlighting its indications and discussing advantages and disadvantages.
Topics: Humans; Composite Resins; Dental Restoration, Permanent; Follow-Up Studies; Female; Dental Caries; Male; Dental Cavity Preparation; Cementation; Dental Materials; Molar; Dental Impression Technique
PubMed: 38905605
DOI: No ID Found -
Primary Dental Journal Jun 2024A technique is outlined for utilising a polymeric composite reinforced with glass fibres in a three-dimensional mesh as a post-core in aesthetic cases. The clinical...
A technique is outlined for utilising a polymeric composite reinforced with glass fibres in a three-dimensional mesh as a post-core in aesthetic cases. The clinical procedure involves obtaining an impression of the root canal space, scanning the definitive cast, and milling a fibre-reinforced composite post-core. Subsequently, the intra-radicular post-core is cemented using an adhesive resin cement. The use of custom-made computer-aided design-computer-aided manufacturing (CAD-CAM) fibre-reinforced composite post-core facilitates repairability, provides better adaptation to the root canal space, avoids uneven cement thickness, ensures chemical adhesion to resin cement, and promotes favourable aesthetics when combined with all-ceramic crowns.
Topics: Computer-Aided Design; Humans; Post and Core Technique; Composite Resins; Dental Prosthesis Design; Glass; Resin Cements; Crowns; Esthetics, Dental; Dental Prosthesis Retention; Dental Materials; Cementation
PubMed: 38888075
DOI: 10.1177/20501684241249546 -
Journal of Dental Research, Dental... 2024This in-vivo study evaluated the accuracy of full-arch digital impressions obtained through different intraoral scanning technologies regarding trueness and efficiency...
BACKGROUND
This in-vivo study evaluated the accuracy of full-arch digital impressions obtained through different intraoral scanning technologies regarding trueness and efficiency against the standard alginate impressions.
METHODS
Alginate impressions were taken from 50 subjects, and the resulting stone casts were scanned using the Trios 3Shape desktop scanner. In-vivo scans were conducted on each participant using three intraoral scanners: Medit, CEREC Primescan, and 3Shape Trios. The scanned files were superimposed onto two software platforms: the 3Shape Orthoanalyser and Geomagic software. This superimposition was performed against the reference model to calculate 3D and 2D deviations, enabling efficiency comparisons between digital and traditional workflows based on work time in minutes. Measurements and comparisons were made in three planes: transverse, sagittal, and vertical dimensions for all the models and stone casts. Statistical analysis employed SPSS 23, with the significance level set at <0.05.
RESULTS
Significant deviations were observed between the three intraoral scanners and the alginate impression, with molar and premolar areas showing greater imprecision across dental arches. Compared to the alginate technique, Medit i500 tended to reduce the transverse dimension in the areas mentioned above, while CEREC exhibited higher precision. Molar and premolar areas emerged as the regions with the greatest discrepancies, both in excess and deficiency, compared to the alginate impression. This difference in dimensions was, however, statistically insignificant overall. 3Shape Trios exhibited the shortest scan times, indicating higher efficiency. Among the intraoral scanners, Medit recorded the longest scanning duration.
CONCLUSION
Accepting the null hypothesis, the scans obtained using all three scanners were comparable with statistically insignificant differences in the measurements. The three scanners differed in the total scan time taken, with the Medit scanner requiring the longest scan time and the 3Shape TRIOS 3 scanner demonstrating the shortest scan duration.
PubMed: 38881640
DOI: 10.34172/joddd.40841 -
Journal of Oral Biology and... 2024To compare the quality of complete dentures and quality of life of participants rehabilitated by using TENS (Transcutaneous electric nerve stimulation) facilitated...
PURPOSE
To compare the quality of complete dentures and quality of life of participants rehabilitated by using TENS (Transcutaneous electric nerve stimulation) facilitated impression making with manual impressions.
MATERIAL AND METHODS
Ten completely edentulous participants were enrolled in the crossover, pilot study. Participants were randomized in 2 groups. Five participants in each group were rehabilitated by dentures fabricated with TENS facilitated definitive impression technique (group T) and conventional impression technique (group C). In group T, Bioelectric border molding was done for the participants, that uses electric stimulation of the nerves supplying the muscles. In group C, incremental border molding using modeling plastic impression compound was carried out. Participants in each group used the dentures for 3 months. After 3 months, OHIP-EDENT questionnaire responses were obtained from the participants to observe the oral health related quality of life. A dental specialist recorded denture quality by Kapur scoring criteria. After one month wash period, the treatment was swapped between the groups. OHIP-EDENT scores and Kapur score were recorded for the alternate dentures after 3 months of use. Descriptive analysis was followed by Mann Whitney test to compare the overall scores between group T and group C for OHIP-EDENT, the scores for individual domains of OHIP-EDENT, and Kapur score for denture evaluation (α = 0.05).
RESULTS
The overall OHIP-EDENT scores within each domain were less in group T when compared with the scores in group C and Kapur score for group T was more than group C. The difference was statistically significant i.e. = 0.002 & 0.003 respectively.
CONCLUSIONS
Less OHIP-EDENT scores in group T imply better perception of quality of life of individuals due to better performance of stomatognathic system. The higher Kapur scores in group T signifies better quality of dentures when TENS was used for definitive impression making.
PubMed: 38855037
DOI: 10.1016/j.jobcr.2024.05.016 -
Journal of International Society of... 2024Internal disc displacement of the temporomandibular joint (TMJ) is identified by an anomaly between the condylar-disc assembly, which, in many cases, may lead to...
Evaluating the Impact of Various Treatment Modalities on the Chewing Efficiency of Anterior Disc Displacements of Temporomandibular Joint Disorder Cases: A Comparative Study.
AIM
Internal disc displacement of the temporomandibular joint (TMJ) is identified by an anomaly between the condylar-disc assembly, which, in many cases, may lead to discomfort and malfunction of the chewing function. The study's objective was to assess the effects of four distinct treatment approaches on temporomandibular disorder cases with anterior disc displacements focusing on their chewing efficiency.
MATERIALS AND METHODS
One hundred participants suffering from reducible TMJ disc displacement were selected for enrollment in the study. Subjects were divided equally into four groups: group I patients were treated with behavioral therapy; group II patients were treated with low-level laser therapy (LLLT); group III patients were treated with anterior repositioning splints; and group IV patients were treated with flat plane splints. Chewing efficiency was assessed utilizing the fractional sieving method and a synthetic food substitute was created using silicon impression material. The statistical analysis encompassed comparisons of chewing efficiency between groups and between baseline and posttreatment within each group, employing analysis of variance (ANOVA) and paired tests, respectively.
RESULTS
Using the paired test, a significant difference in chewing efficiency values as expressed by the median particle size was observed between the baseline and 6-month values in all groups ( < 0.05), except for group I where no significant change was noted over the 6 months ( > 0.05). The one-way ANOVA test revealed a statistically significant difference among groups following therapies ( ˂ 0.05). The Tukey test was employed for pairwise comparisons and revealed statistically significant variances in the main values of chewing efficiency among all groups at a 95% confidence level ( ˂ 0.05).
CONCLUSION
The study's results suggest that occlusal splints and LLLT are more effective in improving chewing efficiency than behavioral interventions.
PubMed: 38827358
DOI: 10.4103/jispcd.jispcd_151_23 -
Journal of Esthetic and Restorative... May 2024To evaluate the compressive modulus, translucency, and light curing irradiance transmittance of four clear polyvinyl siloxane (PVS) materials used for the injection...
OBJECTIVES
To evaluate the compressive modulus, translucency, and light curing irradiance transmittance of four clear polyvinyl siloxane (PVS) materials used for the injection molding technique at varying thicknesses, and to assess the correlation between color parameters and irradiance transmittance.
MATERIALS AND METHODS
Four clear PVS materials (Exaclear, Clear Bite Matrix, Affinity Crystal, and Memosil 2) were used in this study. Compressive modulus was measured by compressing cylindrical PVS specimens (n = 9; d = 10 mm; t = 6 mm) up to 30% strain using a universal testing machine. For the translucency analysis and irradiance transmittance, specimens (n = 5) were fabricated with five different thicknesses (d = 12 mm and t = 2, 4, 6, 8 and 10 mm). The L*, a, *b* values of specimens were obtained using a CIELab spectrophotometer (CMD-700, Konica Minolta) with calibrated white and black tiles; the translucency parameter was calculated. The same specimens were placed onto a spectrophotometer (MARC Light Collector) to measure irradiance transmitted through the specimens from a light curing unit (Valo Corded, Ultradent). Data were analyzed using analysis of variance (ANOVA) with Tukey post hoc test and the correlation between translucency and irradiance transmittance of materials for each thickness was evaluated using Pearson's correlation.
RESULTS
Compressive modulus differences in PVS materials were significant (one-way ANOVA: df = 3, F = 76.27, p < 0.001); Affinity and Memosil 2 were highest with no significant difference between them (Tukey: t = -1.62; p = 0.382). Clear Bite was higher than Exaclear (Tukey: t = -3.70; p = 0.004). Exaclear was lowest. Translucency decreased with thickness (Two-way ANOVA: df = 3, F = 586.53, p < 0.001; thickness: df = 4, F = 1389.34, p < 0.001). Exaclear was most translucent at all thicknesses. L*, a*, b* values varied by material and thickness (L*: df = 3, F = 1213.32, p < 0.001; a*: df = 3, F = 10766.8, p < 0.001; b*: df = 3, F = 3260.42, p < 0.001). Memosil 2 had lowest b* values. Irradiance transmittance was affected by material and thickness (Two-way ANOVA: df = 4, F = 2388.86, p < 0.001). Exaclear had highest irradiance transmission, surpassing control at >6 mm. Violet/blue irradiance ratio decreased with thickness; Exaclear maintained a constant ratio, indicating preserved violet irradiance. There was a strong positive correlation between translucency and light irradiance (Pearson's r = 0.97, R = 0.86-0.96). Radiant exposure analysis suggests adjusting the curing time based on PVS thickness for optimal exposure (10 J/cm) is achievable within 13-14 s for <2 mm and 21-30 s for 8-10 mm with Clear Bite, Affinity, and Memosil 2; whereas Exaclear requires less time.
CONCLUSIONS
Compressive modulus in clear PVS materials varied by type; Affinity and Memosil 2 demonstrate higher modulus, offering more stability of the clear mold. Translucency and irradiance transmission through clear PVS materials decreased as their thickness increased, yet Exaclear exceled in maintaining high translucency and superior light transmission capabilities. Additionally, there is a strong positive linear correlation between translucency and light irradiance transmittance, offering a method to adjust curing times effectively based on material translucency.
CLINICAL SIGNIFICANCE
The light curing time to adequately polymerize composite through clear impression material may need to be increased, particularly with thicker matrices or less translucent materials.
PubMed: 38817077
DOI: 10.1111/jerd.13270 -
Cureus Apr 2024Aim The aim of this in vitro study was to evaluate and compare the accuracy of casts made from two elastomeric impression materials (polyvinyl siloxane (PVS) and...
Aim The aim of this in vitro study was to evaluate and compare the accuracy of casts made from two elastomeric impression materials (polyvinyl siloxane (PVS) and vinylsiloxanether (VSE)) using different impression techniques on parallel and angulated implants. Materials and methods The reference model was fabricated using auto-polymerizing acrylic resin on which three implant analogs were placed of which two were parallel to each other and the third at 20-degree mesial angulation. A total of 60 impressions were made of which 30 were by using PVS and 30 by VSE. For each material, 10 impressions were made by closed tray technique, 10 by open tray technique and 10 by open tray with sandblasting and adhesive coating of the impression copings technique. The inter-analog distances of the casts obtained were evaluated and compared with the reference model by a vision measuring machine. Data were analyzed using analysis of variance (ANOVA), Tukey's Honest Significant Difference (HSD) post hoc and independent samples t-test. Results When the inter-analog distances of the duplicate casts were compared with the reference model, the mean error rates for parallel implants decreased in the order of closed tray technique, open tray technique and open tray with sandblasting and adhesive coating of the impression copings technique for both PVS and VSE impression materials. Similarly, the same order was observed for angulated implants for both impression materials. Using the closed tray technique, there was no statistically significant difference in the accuracy of the cast between the two materials for parallel implants (P = 0.525) and also no significant difference between the two materials for angulated implants (P = 0.307). Similarly, there was no statistically significant difference in the accuracy of the cast between the two materials for parallel implants (P = 0.455) and also no significant difference between the two materials for angulated implants (P = 0.519) using the open tray technique. Whereas for the open tray with sandblasting and adhesive coating of the impression copings technique, VSE produced a more accurate cast than PVS for parallel implants and was statistically significant (P = 0.033); however, there was no significant difference between the two materials for angulated implants (P = 0.375). Conclusion For parallel implants, VSE by an open tray with sandblasting and adhesive coating of the impression copings technique produced a more accurate cast than PVS. For angulated implants, there was no significant difference between the two materials and it was only the technique that significantly affected the accuracy of the cast.
PubMed: 38807829
DOI: 10.7759/cureus.59193 -
European Journal of Dentistry May 2024This study evaluated the linear dimensional change of polymerization of three materials and two techniques of the union of molding transfers for implant-supported...
OBJECTIVES
This study evaluated the linear dimensional change of polymerization of three materials and two techniques of the union of molding transfers for implant-supported prostheses used in the open-tray technique.
MATERIALS AND METHODS
A nylon maxilla-shaped matrix was made, two osseous integrated implants were installed, and, over these two, straight conical mini-pillars were installed. Open-tray impression transfers were attached to the mini-pillars, and a silicone guide was made to standardize the connections between the transfers. The samples were divided into six groups ( = 20): PA (Pattern Resin LS, chemically activated acrylic resin in the single step technique); DU (Durallay, chemically activated acrylic resin in the single step technique); BI (Protemp4, bisacrylic resin in the single step technique); PAC (Pattern Resin LS in sectioning and joining of segments technique); DUC (Durallay, in sectioning and joining of segments technique); and BIC (Protemp4, in sectioning and joining of segments technique). The linear dimensional change values that occurred among these transfers were measured in a profile projector (VB300; Starret) coupled to the Quadra Check device, with a resolution of 0.001 mm, performed by a single calibrated operator.
STATISTICAL ANALYSIS
Data were submitted to a two-way analysis of variance and Tukey's test ( < 0.01).
RESULTS
Statistically significant mean values were found in all comparisons. The PA showed the lowest mean values (µm) of linear dimensional change, both in the single-step technique and in the sectioning and joining technique, in the following order: BI 255.73 (3.81), DU 173.75 (2.30), PA 95.97 (3.20), BIC 23.82 (1.71), DUC 20.85 (2.53), and PAC 13.27 (2.09). The single-step technique showed the worst results, regardless of the material.
CONCLUSION
The sectioning and joining technique reduced the dimensional change in all materials, and the Pattern Resin LS showed the lowest shrinkage mean values, followed by Durallay and Protemp4.
PubMed: 38806161
DOI: 10.1055/s-0044-1779422 -
Cureus May 2024Objective To evaluate and compare the stability of the open tray impression coping within the set impression while attaching the lab analog when polyether (PE) heavy...
Objective To evaluate and compare the stability of the open tray impression coping within the set impression while attaching the lab analog when polyether (PE) heavy body and polyvinyl siloxane (PVS) putty impression materials were used and the implant platform was placed sub-gingivally at three different depths. Methods Two impression materials, PE and PVS, and custom-made plexiglass models with embedded single implants to simulate implant positioning depths of 0 mm, 2 mm, and 4 mm, sub-gingivally, were used in the study. Open tray impressions were made after attaching impression coping to the implant embedded in the model. Implant lab analog was attached to the impression coping in the set impression, and its stability was measured using a universal testing machine. Forty-two open tray impressions were made in six groups, with seven impressions in each group. Descriptive statistics such as mean and standard deviation were calculated. A comparison of the mean stability between the two impression materials at each depth was done using an independent t-test. Comparison of the mean stability between the three different subgingival implant depths in each material was done by one-way ANOVA with the Scheffe multiple comparison test (post-hoc analysis). The level of significance was set at p<0.05. Results The stability of the impression coping was measured as the force in Newtons required for the displacement of the analog attached to the impression coping embedded in the set impression. PE with the embedded impression coping at a depth of 0 mm gave the highest mean stability value (4.37+/-0.41), and the least mean stability was offered by PVS with the embedded impression coping at 4 mm depth (1.88+/-0.37). When an independent t-test was done to compare the mean stability values of PE and PVS, there was a statistically significant difference at 0 mm, 2 mm, and 4 mm. On doing one-way ANOVA to compare the mean stability between the different depth groups, there was a statistically significant difference between the three depth groups in PE and PVS. Scheffe multiple comparison tests (post-hoc analysis) revealed a statistically significant difference between 0 mm, 2 mm, and 4 mm subgingival depths of the impression coping placement in both PE and PVS. Conclusion The accuracy of the master cast is an important determinant for the precise fit and long life of the final prosthesis. In the case of maxillary anterior implant placements where deep subgingival placement of the implant platform is needed for aesthetic and functional reasons, the impression material should be selected carefully to ensure the stability of the impression coping. Among the materials included in the present study, the PE impression material offered the maximum stability for impression coping compared to PVS.
PubMed: 38803409
DOI: 10.7759/cureus.61117