European Journal of Dentistry May 2021The aim of the present study was to evaluate the surface roughness (SR) of various nickel-titanium (NiTi) rotary endodontic instruments (ProTaper Next [PTN], WaveOne...
OBJECTIVES
The aim of the present study was to evaluate the surface roughness (SR) of various nickel-titanium (NiTi) rotary endodontic instruments (ProTaper Next [PTN], WaveOne Gold [WOG], and ProTaper Gold [PTG]) before and after root canal instrumentation.
MATERIALS AND METHODS
For each type (PTN, WOG, and PTG), the endodontic instrumentation was performed using extracted mandibular molar teeth's curved mesial root canals (curvature: 20-40 degrees) after determining the working length. Each NiTi file was cleaned, and sterilized following preparation of four root canals and characterized for surface properties before and after endodontic instrumentation using a contact-mode three-dimensional surface profiler. The data were analyzed statistically using Statistical Package for the Social Sciences for SR parameters including average surface roughness value (Sa), root mean square roughness (Sq), and peak to valley height (Sz).
RESULTS
Preinstrumentation assessment revealed a significant difference for all the three SR variables < 0.05) for the cutting blade and the flute area. WOG instruments showed the highest SR values ( = 0.000). The postinstrumentation assessment revealed significant differences in SR values in the blade and the flute between the three groups ( < 0.05), with WOG and PTG exhibiting the highest values in the blade and flute sections, respectively.
CONCLUSIONS
The SR parameters of intact PTN, WOG, and PTG NiTi files vary and that was increased following the endodontic instrumentation.
PubMed: 33111285
DOI: 10.1055/s-0040-1718469 -
Medicine and Pharmacy Reports Oct 2023The aim of this study is to quantitatively evaluate the effect of different alcoholic and non alcoholic beverages on the tooth enamel surface topography pretreated with...
A comparative evaluation of the effect of alcoholic and non alcoholic beverages on tooth enamel surface pretreated with β-tricalcium phosphate, bioactive glass and amine fluoride: an study.
BACKGROUND AND AIMS
The aim of this study is to quantitatively evaluate the effect of different alcoholic and non alcoholic beverages on the tooth enamel surface topography pretreated with various remineralizing agents using Atomic Force Microscopy.
METHODS
120 tooth specimens were prepared from 60 freshly extracted intact human premolars by sectioning from mesial to distal surfaces using low speed diamond discs and were randomly assigned to study groups and control group. Specimens of Group I, Group II and Group III were pre-treated with β-Tri calcium phosphate, bioactive glass and amine fluoride respectively for 4 minutes for 28 days, followed by storage in artificial saliva. All the specimens were evaluated for surface roughness using Atomic Force Microscopy. The specimens were then placed in alcoholic and non-alcoholic beverages for 10 minutes for 4 days and were again analyzed by Atomic Force Microscopy.Descriptive statistics was performed by using the proportional or frequency distribution of the parameters. The respondents were then grouped according to the branch of specialty if any and the data was evaluated by the one-way ANOVA with post-hoc, with p value <0.005.
RESULTS
In the present study, among the remineralizing agents tested, bioactive glass was found to be more effective than β-Tri Calcium Phosphate and Amine Fluoride. Among the demineralizing agents used in this study, the demineralization potential of Coca Cola was found to be highest, followed by wine and green tea pretreated with β-tricalcium phosphate, bioactive glass and amine fluoride.
CONCLUSIONS
The present study concluded that all the remineralizing agents tested were found to be effective in inhibiting the demineralization caused by various alcoholic and non alcoholic beverages. Among the remineralizing agents tested, bioactive glass was found to be more effective than β-tri calcium phosphate and amine fluoride.
PubMed: 37970202
DOI: 10.15386/mpr-2465 -
Journal of Lasers in Medical Sciences 2016The periodontal therapy is primarily targeted at removal of dental plaque and plaque retentive factors. Although the thorough removal of adherent plaque, calculus and...
Evaluation of the Effects of Er,Cr:YSGG Laser, Ultrasonic Scaler and Curette on Root Surface Profile Using Surface Analyser and Scanning Electron Microscope: An In Vitro Study.
The periodontal therapy is primarily targeted at removal of dental plaque and plaque retentive factors. Although the thorough removal of adherent plaque, calculus and infected root cementum is desirable, it is not always achieved by conventional modalities. To accomplish more efficient results several alternative devices have been used. Lasers are one of the most promising modalities for nonsurgical periodontal treatment as they can achieve excellent tissue ablation with strong bactericidal and detoxification effects. Thirty freshly extracted premolars were selected and decoronated. The mesial surface of each root was divided vertically into four approximately equal parts. These were distributed into four group based on the root surface treatment. Part A (n = 30) was taken as control and no instrumentation was performed. Part B (n = 30) was irradiated by Erbium, Chromium doped Yttrium Scandium Gallium Garnet (Er,Cr:YSGG) laser. Part C (n = 30) was treated by piezoelectric ultrasonic scaler. Part D (n = 30) was treated by Gracey curette. The surface roughness was quantitatively analyzed by profilometer using roughness average (Ra) value, while presence of smear layer, cracks, craters and melting of surface were analyzed using scanning electron microscope (SEM). The means across the groups were statistically compared with control using Dunnett test. Among the test groups, Er,Cr:YSGG laser group showed maximum surface roughness (mean Ra value of 4.14 μm) as compared to ultrasonic scaler (1.727 μm) and curette group (1.22 μm). However, surface with smear layer were found to be maximum (50%) in curette treated samples and minimum (20%) in laser treated ones. Maximum cracks (83.34%) were produced by ultrasonic scaler, and minimum (43.33%) by curettes. Crater formation was maximum (50%) in laser treated samples and minimum (3.33%) in curette treated ones. 63.33% samples treated by laser demonstrated melting of root surface, followed by ultrasonic scaler and curettes. Er,Cr:YSGG laser produced maximum microstructural changes on root surface that can influence the attachment of soft periodontal tissues as well as plaque and calculus deposition. In vivo studies are needed to validate these results and to evaluate their clinical effects.
PubMed: 28491260
DOI: 10.15171/jlms.2016.43 -
Clinical Oral Investigations Feb 2022To investigate tooth wear in young adults, intraoral scanning was used for digital monitoring of the mandibular first molar over 12 months. A possible influence of...
OBJECTIVES
To investigate tooth wear in young adults, intraoral scanning was used for digital monitoring of the mandibular first molar over 12 months. A possible influence of aetiological factors obtained by a questionnaire on tooth wear was investigated.
MATERIALS AND METHODS
A total of 109 participants (mean age at the start of the study: 21.0 ± 2.2 years) were included in this clinical study. At baseline (T0), an intraoral scan (Trios 3, 3Shape) of the study tooth (FDI # 36 or #46) was conducted. After a mean observation period of 373 ± 19 days, a second intraoral scan (T1, n = 94) of the same tooth as at T0 was performed and standard tessellation language datasets were superimposed with 3D analysis software (GOM Inspect). The occlusal surface of the study tooth was divided into 7 areas (5 cusps, 2 ridges) and maximum vertical substance loss was measured between T0 and T1 (n = 91). Three types of tooth wear were defined: cupping (C), facet (F) and combined cupping-facet (CF). Furthermore, a questionnaire on aetiological factors, such as dietary behaviour, was filled out at T0. Data were analysed with non-parametric tests (p < 0.05).
RESULTS
Only one study tooth exhibited no tooth wear at T0, whereas 3 teeth showed C, 47 teeth F and 40 teeth CF. A progression of vertical substance loss for all three types was shown. Most affected were the mesiobuccal cusps (43, 38/47 µm; median, 95%CI) followed by distobuccal (36, 33/39 µm), mesiolingual (35, 26/40 µm), distolingual (34, 27/36 µm) and distal (31, 25/34 µm). On mesial and distal ridges, only F was detected with the lowest vertical substance loss of all areas (mesial ridge: 0, 0/0 µm; distal ridge: 0, 0/0 µm). An association between aetiological factors and loss values could not be shown.
CONCLUSIONS
All study teeth showed clear signs of wear, and after only 1 year, further substance loss was detectable. This result is of significance for young adults.
CLINICAL RELEVANCE
Since data of young adults regarding tooth wear are scarce, the results give a first idea of the amount of vertical loss per year and its relation to aetiological factors such as dietary behaviour. Therefore, further studies over a longer observation period are highly recommended.
Topics: Humans; Incisor; Molar; Tooth Attrition; Tooth Wear; Young Adult
PubMed: 34498100
DOI: 10.1007/s00784-021-04162-6 -
Clinical and Experimental Dental... Feb 2022This study aimed to assess the enamel and dentin marginal microleakage and dentin microtensile bond strength (μTBS) of ACTIVA BioACTIVE Restorative with and without a...
OBJECTIVES
This study aimed to assess the enamel and dentin marginal microleakage and dentin microtensile bond strength (μTBS) of ACTIVA BioACTIVE Restorative with and without a bonding agent compared with conventional restorative materials.
MATERIAL AND METHODS
For enamel and dentin microleakage, Class II boxes were prepared in the mesial (1 mm under the cementoenamel junction) and distal (1 mm above the cementoenamel junction) surfaces of 90 extracted human third molars. The teeth were randomly divided into five groups (n = 18): Group Z (G-Premio Bond + Filtek Z250 XT), Group X (G-Premio Bond + X-tra fil bulk-fill), Group AA (G-Premio Bond + Activa Bioactive restorative), Group A (Activa Bioactive restorative), and Group G (dentin conditioner + Fuji II LC Improve). The teeth were thermocycled, and their microleakage was quantified using the dye penetration test under a stereomicroscope. For dentin μTBS measurement, 12 specimens were fabricated in metal molds (1 × 1 × 12 mm³) for each group mentioned above, and a universal testing machine measured their μTBS. Data were analyzed using one-way analysis of variance (ANOVA), the Kruskal-Wallis test, and multiple comparisons tests.
RESULTS
Significant differences were noted among the groups in marginal microleakage and μTBS (p < .001). The highest mean microleakage scores at the enamel and dentin margins were noted in Group A, which had significant differences with other groups (p < .001). The highest μTBS was found in Group X, with significant differences with Group G and Group A (p < .05). The lowest µTBS was noted in Group A, with significant differences with Groups X, Group AA, and Group Z (p < .001).
CONCLUSIONS
Activa Bioactive without a bonding agent showed significantly lower µTBS to dentin, and higher microleakage at the enamel and dentin margins. Application of adhesive resin with Activa Bioactive provided a dentine bond strength and marginal seal comparable to other restorative materials.
Topics: Dental Cements; Dental Leakage; Dental Restoration, Permanent; Humans; Resin Cements; Tooth Cervix
PubMed: 35037730
DOI: 10.1002/cre2.534 -
Progress in Orthodontics 2016An important constituent of an orthodontic appliance is orthodontic brackets. It is either the bracket or the archwire that slides through the bracket slot, during...
BACKGROUND
An important constituent of an orthodontic appliance is orthodontic brackets. It is either the bracket or the archwire that slides through the bracket slot, during sliding mechanics. Overcoming the friction between the two surfaces demands an important consideration in an appliance design. The present study investigated the surface roughness of four different commercially available stainless steel brackets.
METHODS
All tests were carried out to analyse quantitatively the morphological surface of the bracket slot floor with the help of scanning electron microscope (SEM) machine and to qualitatively analyse the average surface roughness (Sa) of the bracket slot floor with the help of a three-dimensional (3D) non-contact optical surface profilometer machine.
RESULTS
The SEM microphotographs were evaluated with the help of visual analogue scale, the surface roughness for group A = 0-very rough surface, group C = 1--rough surface, group B = 2--smooth surface, and group D = 3-very smooth surface. Surface roughness evaluation with the 3D non-contact optical surface profilometer machine was highest for group A, followed by group C, group B and group D. Groups B and D provided smooth surface roughness; however, group D had the very smooth surface with values 0.74 and 0.75 for mesial and distal slots, respectively.
CONCLUSIONS
Evaluation of surface roughness of the bracket slot floor with both SEM and profilometer machine led to the conclusion that the average surface roughness was highest for group A, followed by group C, group B and group D.
Topics: Friction; Imaging, Three-Dimensional; Materials Testing; Orthodontic Appliance Design; Orthodontic Brackets; Orthodontic Wires; Stainless Steel; Surface Properties
PubMed: 26763529
DOI: 10.1186/s40510-016-0116-2 -
Journal of International Society of... 2021The aim of this investigation was to detect defects that may occur to Reciproc endodontic files after a single use.
OBJECTIVE
The aim of this investigation was to detect defects that may occur to Reciproc endodontic files after a single use.
MATERIALS AND METHODS
A sample of convenience of Reciproc files (VDW GmbH, Munich, Germany) that were used to prepare root canals of anterior or posterior teeth were collected. The files were divided equally into two groups: Group 1 (R25) files were used to prepare mesial root canals of 50 human permanent mandibular molars, and Group 2 (R40) included 50 files that were used to prepare permanent maxillary incisor teeth. Files were analyzed after single use by using a scanning electron microscope at X120 to detect changes in surface morphology. The data were statistically analyzed by using the χ test, and statistical significance was set at < 0.05.
RESULTS
A total of 96 Reciproc NiTi files were collected; of those, 67 (70%) were unaffected and 29 (30%) showed overall surface deformations. The types of deformation were blade disruption (22%), surface pitting (12%), and unwinding and tip deformation (1%). No microcracks were detected, and none of the studied files showed fracture. R40 was three times more likely to be deformed and showed blade disruption compared with R25 ( < 0.05).
CONCLUSIONS
Reciproc rotary NiTi files show high resistance to deformation after a single use. Blade disruption was the most frequent defect occurring in both the small and large files.
PubMed: 33688479
DOI: 10.4103/jispcd.JISPCD_412_20 -
Brazilian Oral Research 2020This study analyzed the effect of prior application of copaiba oil (CO) emulsions as a dentin cleaning substance on microleakage and microtensile adhesive strength....
This study analyzed the effect of prior application of copaiba oil (CO) emulsions as a dentin cleaning substance on microleakage and microtensile adhesive strength. Twenty-five premolars and sixty-four molars were used for microleakage and microtensile assays. For the microleakage assays, specimens with standard class V cavities were divided (n = 5), according to the tested CO emulsions: CO10%X, CO10%Y, and CO10%Z, as well as chlorhexidine 2% (CHX) and distilled water (DW), as positive and negative controls, respectively. Restorations were performed using the Adper Single Bond® and/or Clearfil SE Bond® systems. Cervical, occlusal, distal and mesial sections were assessed for tracer penetration degree at the composite/tooth interface. For the microtensile assay, healthy molars were divided into sixteen groups, in which artificial caries were induced in half of the groups. Dentin surfaces were treated with CO10%X and CO10%Y, CHX and DW. Microtensile bond strength was measured by fixing each sample to the plate of a universal testing machine operated at a speed of 0.5 mm/minute until failure. Dentin treated with CO10%X showed a lower infiltration rate than dentin treated with the other CO emulsions, CHX2% and DW. According to the microtensile assay, both healthy and affected dentin treated with CO10%X and Adper Single Bond® adhesive system presented higher adhesive strength. CO emulsion, used as a dentin biomodifier, interfered positively in microleakage and improved adhesive strength after acid etching in the Adper Single Bond® adhesive system, or before applying the Clearfil SE Bond® self-etching system.
Topics: Analysis of Variance; Chlorhexidine; Composite Resins; Dental Bonding; Dental Cements; Dental Leakage; Dentin; Dentin-Bonding Agents; Emulsions; Fabaceae; Humans; Materials Testing; Plant Oils; Reproducibility of Results; Resin Cements; Statistics, Nonparametric; Surface Properties; Tensile Strength
PubMed: 32022221
DOI: 10.1590/1807-3107bor-2020.vol34.0001 -
Journal of Oral Science Oct 2021To evaluate the influence of the restorative material and matrix system on proximal contact tightness and morphological characteristics of class II restorations in...
PURPOSE
To evaluate the influence of the restorative material and matrix system on proximal contact tightness and morphological characteristics of class II restorations in primary molars.
METHODS
Occluso-mesial cavities in second primary artificial molars were randomly restored using different materials (Filtek Z500 or Filtek Bulk Fill composites or high-viscosity glass ionomer cement Ketac Universal) and different matrix system (Tofflemire, AutoMatrix, matrix band with ring, contoured sectional matrix) (n = 12). Proximal contact tightness was measured using a custom-made device in an Instron 3345, and proximal surface morphology and marginal adaptation were scored after digital scanning. Two-way ANOVA, Tukey and Fischer's exact tests were performed (P < 0.05).
RESULTS
Proximal contact tightness values were significantly influenced by the restorative material (P < 0.05), the matrix system (P < 0.001), and their interaction (P < 0.01). Both resin composites showed statistically differences in proximal shape according to the matrix used to restore and exhibited overhanging margins. Ketac Universal restorations showed similar morphology and gaps on the margins regardless of the matrix system.
CONCLUSIONS
Overall, both composite restorations achieved tighter proximal contact than those restored with the high-viscosity glass ionomer cement. None of the matrix systems tested provided a convex seamless proximal morphology.
Topics: Dental Materials; Glass Ionomer Cements; Molar; Tooth, Deciduous; Viscosity
PubMed: 34511588
DOI: 10.2334/josnusd.21-0264 -
Scientific Reports Nov 2021This retrospective pilot study used a newly developed evaluation tool to assess the prevalence and incidence of White Spot Lesions (WSL) before and after multibracket...
This retrospective pilot study used a newly developed evaluation tool to assess the prevalence and incidence of White Spot Lesions (WSL) before and after multibracket appliance (MB) therapy. Digital photographs of 121 adolescent patients (63 ♂, 58 ♀) with metal brackets were analyzed retrospectively before and after MB therapy. The labial surfaces of anterior teeth, canine teeth, and premolars in the upper (UJ) and lower jaws (LJ) were evaluated using the Enamel Decalcification Index (EDI) by Banks and Richmond (Eur J Orthod, 16(1):19-25, 1994, levels 0-3) and a specially developed digitally scaled graticule with concentric circles to quantify the extent of WSL (in %). The statistical data analysis was based on crosstabulations and logistic regression. Before MB, 69.4% of the patients presented at least one WSL and 97.5% after, an increase of 28.1%. Before MB, 18.4% of the tooth surfaces (TS) showed an EDI level of 1-3. After MB, 51.8% of the TS featured WSL. 18.2% of the TS showed a WSL to the extent of ≥ 20-100% before and 52.3% after MB. The incidence in the UJ (71-79%) as well as the LJ (64-76%) was highest for the first and second premolars and lowest for LJ incisors (22-35%). The probability for developing a new distal WSL is higher than developing gingival, mesial or occlusal WSL. Labial MB therapy drastically increases the risk of developing WSL. We verified a concise quantification of the extent of labial WSL with the evaluation index.
Topics: Adolescent; Dental Caries; Dental Caries Susceptibility; Female; Humans; Male; Orthodontic Brackets; Photography, Dental; Pilot Projects; Retrospective Studies; Tooth Demineralization
PubMed: 34725354
DOI: 10.1038/s41598-021-00561-7